| Βιβλιογραφική Αναφορά | K. Komnitsas, E. Petrakis, O. Pantelaki and A. Kritikaki, "Column leaching of greek low-grade limonitic laterites," Minerals, vol. 8, no. 9, Aug. 2018. doi: 10.3390/min8090377 https://doi.org/10.3390/min8090377 | ||
| Εμφανίζεται στις Συλλογές |
In this study, column leaching experiments were carried out to investigate the extraction of Ni and Co from low-grade limonitic laterites from Agios Ioannis mines in central Greece. Tests were carried out in laboratory Plexiglas columns usingH2SO4 as leaching solution. Parameters determining the efficiency of the process, i.e., acid concentration (0.5 M or 1.5 M) and addition of 20 or 30 g/Lof sodium sulfite (Na2SO3) in the leaching solution, were also studied. Upflow transport of the leaching solution with the use of peristaltic pumps was carried out, while the pregnant leach solution (PLS) was recycled several times over the entire test duration. The concentration of Ni, Co, Fe, Ca, Al, Mg, and Mn in the PLS was determined by Atomic Absorption Spectroscopy (AAS). The oreand the leaching residues were characterized by different techniques, i.e., X-ray fluorescence (XRF), X-ray diffraction (XRD), Fourier transform infrared (FTIR) spectroscopy, and differential scanning calorimetry and thermogravimetry (DSC/TG). The experimental results showed that (i) Ni and Co extractions increased with the increase of H2SO4 concentration—60.2% Ni and 59.0% Co extractions were obtained after 33 days of leaching with 1.5 M H2SO4; (ii) addition of 20 g/L Na2SO3 in the leaching solution resulted in higher extraction percentages for both metals (73.5% for Ni and 84.1% for Co, respectively), whereas further increase of Na2SO3 concentration to 30 g/L only marginally affected Ni and Co extractions; and (iii) when leaching was carried out with 1.5 M H2SO4 and 20 g/L Na2SO3, its selectivity was improved, as deduced from the ratios Ni/Mg, Ni/Ca and Ni/Al in the PLS; on the other hand, the ratio Ni/Fe dropped as a result of the higher Fe extraction compared with that of Ni.
Copyright © DIAS 2013